點擊圖片查看大圖食品級擠出ABS CYCOLAC EX58F 高粘度ABS
High impact ABS for sheet extrusion and blow molding applications. FDA food contact compliant.
用于板材擠壓和吹塑應用的高沖擊ABS。符合FDA食品接觸標準。
EX58F物性表：
| REVISION: 09/07/2019 Compare this region | ||||
|---|---|---|---|---|
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 39 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 30 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3.1 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 32 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 2080 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 66 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2160 | MPa | ASTM D 790 | |
| Hardness, Rockwell R | 102 | - | ASTM D 785 | |
| Tensile Stress, yield, 50 mm/min | 41 | MPa | ISO 527 | |
| Tensile Stress, break, 50 mm/min | 30 | MPa | ISO 527 | |
| Tensile Strain, yield, 50 mm/min | 2.6 | % | ISO 527 | |
| Tensile Strain, break, 50 mm/min | 21 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 1970 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 60 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 2000 | MPa | ISO 178 | |
| IMPACT | ||||
| Izod Impact, notched, 23°C | 432 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 299 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 37 | J | ASTM D 3763 | |
| Izod Impact, notched 80*10*4 +23°C | 35 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 23 | kJ/m2 | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 37 | kJ/m2 | ISO 179/1eA | |
| THERMAL | ||||
| Vicat Softening Temp, Rate B/50 | 106 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 91 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 76 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 1.01E-04 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 1.04E-04 | 1/°C | ASTM E 831 | |
| Vicat Softening Temp, Rate B/50 | 95 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 97 | °C | ISO 306 | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 78 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.03 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm | 0.6-0.8 | % | SABIC method | |
| Melt Viscosity, 240°C, 100 sec-1 | 15500 | Poise | ASTM D 3825 | |
| Density | 1.03 | g/cm3 | ISO 1183 | |
| Melt Flow Rate, 220°C/10.0 kg | 4 | g/10 min | ISO 1133 | |
| ELECTRICAL | ||||
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 4 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 4 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A | |
| FLAME CHARACTERISTICS | ||||
| UL Yellow Card | E45329-103353495 | - | - | |
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 | |
| SHEET EXTRUSION | ||||
| Drying Temperature | 80-95 | °C | ||
| Drying Time | 4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 215-260 | °C | ||
| Barrel - Zone 1 Temperature | 170-200 | °C | ||
| Barrel - Zone 2 Temperature | 180-220 | °C | ||
| Barrel - Zone 3 Temperature | 190-225 | °C | ||
| Barrel - Zone 4 Temperature | 200-240 | °C | ||
| Adapter Temperature | 205-250 | °C | ||
| Die Temperature | 205-250 | °C | ||
| Roll Stack Temp - Top | 90-95 | °C | ||
| Roll Stack Temp - Middle | 95-105 | °C | ||
| Roll Stack Temp - Bottom | 100-105 | °C | ||