點擊圖片查看大圖CYCOLAC MG29 高沖擊ABS 良好的低溫韌性
Super high impact ABS. Good low temperature toughness.ASIAAMERICAS
超高沖擊ABS。良好的低溫韌性。
MG29物性表：
| REVISION: 24/09/2019 Compare this region | ||||
|---|---|---|---|---|
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 39 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 31 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 2.4 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 26 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 2000 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 65 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2070 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 50 mm/min | 42 | MPa | ISO 527 | |
| Tensile Stress, break, 50 mm/min | 32 | MPa | ISO 527 | |
| Tensile Strain, yield, 50 mm/min | 2.8 | % | ISO 527 | |
| Tensile Strain, break, 50 mm/min | 20 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 2050 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 61 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 1990 | MPa | ISO 178 | |
| IMPACT | ||||
| Izod Impact, notched, 23°C | 455 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 29 | J | ASTM D 3763 | |
| Izod Impact, notched 80*10*4 +23°C | 37 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 12 | kJ/m2 | ISO 180/1A | |
| THERMAL | ||||
| Vicat Softening Temp, Rate B/50 | 99 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 94 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 79 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 9.54E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 9.36E-05 | 1/°C | ASTM E 831 | |
| Vicat Softening Temp, Rate B/50 | 98 | °C | ISO 306 | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 79 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.04 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.8 | % | SABIC method | |
| Melt Flow Rate, 230°C/3.8 kg | 1.2 | g/10 min | ASTM D 1238 | |
| Melt Viscosity, 240°C, 1000 sec-1 | 2800 | Poise | ASTM D 3825 | |
| Melt Flow Rate, 220°C/10.0 kg | 8 | g/10 min | ISO 1133 | |
| ELECTRICAL | ||||
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 3 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 0 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 1 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 | |
| INJECTION MOLDING | ||||
| Drying Temperature | 90-95 | °C | ||
| Drying Time | 2-4 | hrs | ||
| Drying Time (Cumulative) | 8 | hrs | ||
| Maximum Moisture Content | 0.1 | % | ||
| Melt Temperature | 230-275 | °C | ||
| Nozzle Temperature | 230-275 | °C | ||
| Front - Zone 3 Temperature | 225-240 | °C | ||
| Middle - Zone 2 Temperature | 210-220 | °C | ||
| Rear - Zone 1 Temperature | 190-200 | °C | ||
| Mold Temperature | 50-65 | °C | ||
| Back Pressure | 0.3-0.7 | MPa | ||
| Screw Speed | 30-60 | rpm | ||
| Shot to Cylinder Size | 50-70 | % | ||
| Vent Depth | 0.038-0.051 | mm | ||