| SABIC Innovative Plastics LNP STAT-LOY AX11421 ABS | |||
|---|---|---|---|
| Categories: |
Polymer; Thermoplastic; ABS Polymer
|
||
| Material Notes: |
LNP* STAT-LOY* AX11421 is a compound based on ABS resin. Added feature of this material is: Antistatic.
|
||
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. | ||
|
|||
Printer friendly version
Download as PDF
Download to Excel (requires Excel and Windows)
Export data to your CAD/FEA program| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Density | 1.05 g/cc | 0.0379 lb/in3 | ASTM D792 |
| Moisture Absorption | 2.00 % | 2.00 % | 50% RH, 24 hrs; ASTM D570 |
| 3.70 % | 3.70 % | 23°C / 50% RH; ISO 62 | |
Linear Mold Shrinkage, Flow 
|
0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
|
0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ISO 294 | |
|
Linear Mold Shrinkage, Transverse
|
0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
|
0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 21.0 MPa | 3050 psi | Type I, 5 mm/min; ASTM D638 |
| 21.0 MPa | 3050 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | Type I, 5 mm/min; ASTM D638 |
| 30.0 MPa | 4350 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 48 % | 48 % | Type I, 5 mm/min; ASTM D638 |
| 81 % | 81 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 4.4 % | 4.4 % | 5 mm/min; ISO 527 |
| 4.7 % | 4.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 1.31 GPa | 190 ksi | 1 mm/min; ISO 527 |
| 1.41 GPa | 205 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 44.0 MPa | 6380 psi | ISO 178 |
| Flexural Yield Strength | 44.0 MPa | 6380 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.33 GPa | 193 ksi | 2 mm/min; ISO 178 |
| 1.35 GPa | 196 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 4.25 J/cm | 7.96 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 39.0 kJ/m2 | 18.6 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy |
29.0 J @Temperature 23.0 °C |
21.4 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 20.0 J | 14.8 ft-lb | Multiaxial Impact; ISO 6603 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1.00e+7 - 1.00e+9 ohm | 1.00e+7 - 1.00e+9 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow |
113 μm/m-°C @Temperature -30.0 - 30.0 °C |
62.8 μin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow |
126 μm/m-°C @Temperature -30.0 - 30.0 °C |
70.0 μin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
69.0 °C @Thickness 3.20 mm |
156 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 |
HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.
Users viewing this material also viewed the following:
Covestro Bayblend? T65 XF Polycarbonate + ABS
SABIC Innovative Plastics LNP STAT-LOY A3000T ABS
SABIC Innovative Plastics LNP THERMOCOMP AB002 ABS
Techmer ES Electrablend? ABS 03008 Stainless Steel Filled
Covestro Bayblend? T65 AT PC/ABS Blend
免責聲明：（1）以上所展示的信息由企業自行提供，內容的真實性、準確性和合法性由發布企業負責，環球塑化網對此不承擔任何保證責任。我們原則上建議您優先選擇“塑企通”會員合作! （2）同時我們鄭重提醒各位買/賣家，交易前請詳細核實對方身份，切勿隨意打款或發貨，謹防上當受騙。如發現虛假信息，請向環球塑化網舉報。
簡繁切換