點(diǎn)擊圖片查看大圖
LNP* STAT-LOY* A3000LTH is a compound based on ABS resin. Added features of this material include: Transparent, Antistatic, Formulation Locked.
SABIC Innovative Plastics LNP STAT-LOY A3000LTH ABS
Categories:
Polymer; Thermoplastic; ABS Polymer
Material Notes:
LNP* STAT-LOY* A3000LTH is a compound based on ABS resin. Added features of this material include: Transparent, Antistatic, Formulation Locked.
Vendors:
No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
Printer friendly version 
Download as PDF 
Download to Excel (requires Excel and Windows)
Export data to your CAD/FEA program
Add to Folder: My Folder
Physical Properties
Metric
English
Comments
Specific Gravity
1.09 g/cc
1.09 g/cc
ASTM D792
Density
1.08 g/cc
0.0390 lb/in3
ASTM D792
Moisture Absorption
0.520 %
0.520 %
50% RH, 24 hrs; ASTM D570
0.800 %
0.800 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow
0.0050 - 0.0070 cm/cm
@Time 86400 sec
0.0050 - 0.0070 in/in
@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse
0.0070 - 0.0090 cm/cm
@Time 86400 sec
0.0070 - 0.0090 in/in
@Time 24.0 hour
ASTM D955
Mechanical Properties
Metric
English
Comments
Tensile Strength at Break
27.0 MPa
3920 psi
Type I, 5 mm/min; ASTM D638
28.0 MPa
4060 psi
5 mm/min; ISO 527
Tensile Strength, Yield
37.0 MPa
5370 psi
5 mm/min; ISO 527
38.0 MPa
5510 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break
33 %
33 %
Type I, 5 mm/min; ASTM D638
37 %
37 %
5 mm/min; ISO 527
Elongation at Yield
3.8 %
3.8 %
5 mm/min; ISO 527
3.9 %
3.9 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus
1.60 GPa
232 ksi
1 mm/min; ISO 527
1.68 GPa
244 ksi
5 mm/min; ASTM D638
Flexural Strength
52.0 MPa
7540 psi
ISO 178
Flexural Yield Strength
56.0 MPa
8120 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus
1.56 GPa
226 ksi
2 mm/min; ISO 178
1.66 GPa
241 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched
1.70 J/cm
3.18 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO)
15.0 kJ/m2
7.14 ft-lb/in2
80*10*4; ISO 180/1A
Dart Drop, Total Energy
34.0 J
@Temperature 23.0 °C
25.1 ft-lb
@Temperature 73.4 °F
ASTM D3763
Impact Test
26.0 J
19.2 ft-lb
Multiaxial Impact; ISO 6603
Electrical Properties
Metric
English
Comments
Surface Resistance
1.00e+9 - 1.00e+11 ohm
1.00e+9 - 1.00e+11 ohm
ASTM D257
Thermal Properties
Metric
English
Comments
CTE, linear, Parallel to Flow
106 μm/m-°C
@Temperature -30.0 - 30.0 °C
58.9 μin/in-°F
@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow
113 μm/m-°C
@Temperature -30.0 - 30.0 °C
62.8 μin/in-°F
@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)
76.0 °C
169 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
78.0 °C
@Thickness 3.20 mm
172 °F
@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)
63.0 °C
145 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
65.0 °C
@Thickness 3.20 mm
149 °F
@Thickness 0.126 in
unannealed; ASTM D648
Optical Properties
Metric
English
Comments
Transmission, Visible
90 %
90 %
transparent; thickness not quantified
Users viewing this material also viewed the following:
Ebbtide Polymers 900 Transparent ABS
LG Chemical TR551 MABS, High Transparency, High Rigidity, High Hardness
LNP Cycolac? SLA5853 Acrylonitrile Butadiene Styrene
Styrolution Terlux? 2802 TR Q434 Transparent MABS
PlastxWorld CEVIAN?-V T150 ABS