| SABIC Innovative Plastics LNP STAT-KON AE003 ABS | |||
|---|---|---|---|
| Categories: |
Polymer; Thermoplastic; ABS Polymer
|
||
| Material Notes: |
LNP STAT-KON* AE003 is a compound based on ABS resin containing 15% Carbon Fiber. Added feature of this material is: Electrically Conductive.
|
||
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. | ||
|
|||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Density | 1.14 g/cc | 0.0412 lb/in3 | ASTM D792 |
| Moisture Absorption | 0.250 % | 0.250 % | 50% RH, 24 hrs; ASTM D570 |
| 0.250 % | 0.250 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow |
0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse |
0.0030 - 0.0060 cm/cm @Time 86400 sec |
0.0030 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 |
| 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 12.96 GPa | 1880 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 131 MPa | 19000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 152 MPa | 22000 psi | ISO 178 | |
| Flexural Modulus | 10.61 GPa | 1539 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 12.75 GPa | 1849 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.20 J/cm | 5.99 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m2 | 2.86 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 16.0 kJ/m2 | 7.61 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow |
20.3 μm/m-°C @Temperature -30.0 - 30.0 °C |
11.3 μin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow |
71.5 μm/m-°C @Temperature -30.0 - 30.0 °C |
39.7 μin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb'sterms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.
Users viewing this material also viewed the following:
SABIC Innovative Plastics LNP STAT-KON AX02747 ABS
SABIC Innovative Plastics LNP STAT-KON AX01706 ABS
SABIC Innovative Plastics LNP STAT-KON AE008XXY ABS
SABIC Innovative Plastics LNP STAT-KON AE006 ABS
SABIC Innovative Plastics LNP STAT-KON AE003 ABS (Europe-Africa-Middle East)
免責聲明：（1）以上所展示的信息由企業自行提供，內容的真實性、準確性和合法性由發布企業負責，環球塑化網對此不承擔任何保證責任。我們原則上建議您優先選擇“塑企通”會員合作! （2）同時我們鄭重提醒各位買/賣家，交易前請詳細核實對方身份，切勿隨意打款或發貨，謹防上當受騙。如發現虛假信息，請向環球塑化網舉報。
簡繁切換