| DuPont Performance Polymers Zytel? HTN54G15HSLR BK031 PA-IGF15 | |||
|---|---|---|---|
| Categories: | Polymer; Thermoplastic; Polyphthalamide (PPA); Polyphthalamide (PPA), 20% Glass Fiber Reinforced | ||
| Material Notes: |
15% Glass Reinforced, Toughened, PPA, High Performance Polyamide
Information provided by DuPont Performance Polymers |
||
| Vendors: |
Click here to view all available suppliers for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. |
||
|
|||
Printer friendly version
Download as PDF
Download to Excel (requires Excel and Windows)
Export data to your CAD/FEA program| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in3 | DAM; ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.00400 cm/cm | 0.00400 in/in | DAM; ISO 294-4, 2577 | ||
| 0.00700 cm/cm | 0.00700 in/in | DAM; ISO 294-4, 2577 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 118 MPa | 17100 psi | 50%RH; ISO 527-1/-2 | ||
| 125 MPa | 18100 psi | DAM; ISO 527-1/-2 | |||
| Elongation at Break | 3.00 % | 3.00 % | 50%RH; ISO 527-1/-2 | ||
| 3.50 % | 3.50 % | DAM; ISO 527-1/-2 | |||
| Tensile Modulus | 5.50 GPa | 798 ksi | DAM; ISO 527-1/-2 | ||
| 6.10 GPa | 885 ksi | 50%RH; ISO 527-1/-2 | |||
| Flexural Strength | 210 MPa | 30500 psi | DAM; ISO 178 | ||
| Flexural Modulus | 4.90 GPa | 711 ksi | DAM; ISO 178 | ||
| Charpy Impact Unnotched |
6.00 J/cm2 @Temperature 23.0 °C |
28.6 ft-lb/in2 @Temperature 73.4 °F |
DAM; ISO 179/1eU | ||
Charpy Impact, Notched 
|
0.500 J/cm2 @Temperature -40.0 °C |
2.38 ft-lb/in2 @Temperature -40.0 °F |
DAM; ISO 179/1eA | ||
|
0.600 J/cm2 @Temperature 23.0 °C |
2.86 ft-lb/in2 @Temperature 73.4 °F |
DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DAM; IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 34.0 μm/m-°C | 18.9 μin/in-°F | DAM; ISO 11359-1/-2 | ||
|
34.0 μm/m-°C @Temperature -40.0 - 23.0 °C |
18.9 μin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 73.0 μm/m-°C | 40.6 μin/in-°F | DAM; ISO 11359-1/-2 | ||
|
|
70.0 μm/m-°C @Temperature -40.0 - 23.0 °C |
38.9 μin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 | ||
| Melting Point | 300 °C | 572 °F | first heat; DAM; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 277 °C | 531 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | DAM; ISO 75-1/-2 | ||
|
Flammability, UL94
|
HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; IEC 60695-11-10 | ||
|
HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
DAM; IEC 60695-11-10 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | >= 320 °C | >= 608 °F | |||
| 325 °C | 617 °F | Optimum | |||
| <= 330 °C | <= 626 °F | ||||
| Mold Temperature | >= 85.0 °C | >= 185 °F | |||
| <= 105 °C | <= 221 °F | ||||
| Drying Temperature |
100 °C @Time 21600 - 28800 sec |
212 °F @Time 6.00 - 8.00 hour |
|||
| Moisture Content | 0.100 % | 0.100 % | |||
|
De |
|||||
| Drying Recommended | yes | ||||
| Part Marking Code | >PA-IGF15< | ISO 11469 | |||
| >PPA-IGF15< | SAE J1344 | ||||
| Processing | Injection Molding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PA-IGF15 | ISO 1043 | |||
| Special characteristics | Heat stabilized or stable to heat | ||||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb'sterms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.
Users viewing this material also viewed the following:
DuPont Performance Polymers Zytel? HTN54G35EF BK420 PA-IGF35
DuPont Performance Polymers Zytel? HTN54G15HSLR NC010 PA-IGF15
DuPont Performance Polymers Zytel? HTN53G60LRHF BK083 PA-GF60
DuPont Performance Polymers Zytel? HTN53G50LWSF BK702A HTN (PA)
DuPont Performance Polymers Zytel? HTN53G50HSLR NC010 PA-GF50
 
|
||
|
PPA性能描述:改性聚對二酰對二胺PPA塑料的熱變形溫度高達300℃以上，連續使用溫度可達170℃，能滿足您所需的短期和長期的熱性能。它可在寬廣的溫度范圍內和高濕度環境中保持其優越的機械性特性—強度、硬度、耐疲勞性及抗蠕變性。增韌呂級PPA結合優越的韌度與一定范圍的硬度和柔性，在扣件中要求一次性使用的剛性、以及重復性使用中撓屈性的良好選擇。同時提供特殊品級的產品應用于可噴涂和可電鍍的表面，防火性、耐乙二醇性及反身性要求的應用. 主要應用: 汽車部件，包括燃油、傳動及發動機系統，可減輕重量、降低成本并提供長時間的使用壽命； 芯片組和插座、杯體焊接支座； 片狀電容器、開關及微型喇叭、制作高密度的印刷電路板連接器； 用于耐磨要求極高的場合，例如無潤滑軸承、密封、軸承隔離環和往復開壓縮機零件； |
|