| DuPont Performance Polymers Zytel? HTN51G45HSL BK083 PA6T/XT-GF45 | |||
|---|---|---|---|
| Categories: | Polymer; Thermoplastic; Polyphthalamide (PPA); Polyphthalamide (PPA), 50% Glass Fiber Reinforced | ||
| Material Notes: |
45% Glass Reinforced, PPA, High Performance Polyamide
Information provided by DuPont Performance Polymers |
||
| Vendors: |
Click here to view all available suppliers for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. |
||
|
|||
Printer friendly version
Download as PDF
Download to Excel (requires Excel and Windows)
Export data to your CAD/FEA program| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in3 | DAM; ISO 1183 | ||
| Water Absorption |
3.60 % @Thickness 2.00 mm |
3.60 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Moisture Absorption |
1.00 % @Thickness 2.00 mm |
1.00 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.00200 cm/cm | 0.00200 in/in | DAM; ISO 294-4, 2577 | ||
| 0.00600 cm/cm | 0.00600 in/in | DAM; ISO 294-4, 2577 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 230 MPa | 33400 psi | 50%RH; ISO 527-1/-2 | ||
| 240 MPa | 34800 psi | DAM; ISO 527-1/-2 | |||
| Elongation at Break | 2.00 % | 2.00 % | 50%RH; ISO 527-1/-2 | ||
| 2.30 % | 2.30 % | DAM; ISO 527-1/-2 | |||
| Tensile Modulus | 15.0 GPa | 2180 ksi | DAM; ISO 527-1/-2 | ||
| 15.5 GPa | 2250 ksi | 50%RH; ISO 527-1/-2 | |||
| Flexural Modulus | 13.2 GPa | 1910 ksi | DAM; ISO 178 | ||
Izod Impact, Notched (ISO) 
|
12.0 kJ/m2 @Temperature 23.0 °C |
5.71 ft-lb/in2 @Temperature 73.4 °F |
DAM; ISO 180/1A | ||
|
13.0 kJ/m2 @Temperature -40.0 °C |
6.19 ft-lb/in2 @Temperature -40.0 °F |
DAM; ISO 180/1A | |||
|
Charpy Impact Unnotched
|
8.00 J/cm2 @Temperature -30.0 °C |
38.1 ft-lb/in2 @Temperature -22.0 °F |
DAM; ISO 179/1eU | ||
|
8.50 J/cm2 @Temperature 23.0 °C |
40.4 ft-lb/in2 @Temperature 73.4 °F |
DAM; ISO 179/1eU | |||
|
Charpy Impact, Notched
|
1.20 J/cm2 @Temperature 23.0 °C |
5.71 ft-lb/in2 @Temperature 73.4 °F |
DAM; ISO 179/1eA | ||
|
1.20 J/cm2 @Temperature -30.0 °C |
5.71 ft-lb/in2 @Temperature -22.0 °F |
DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | DAM; IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 300 °C | 572 °F | first heat; DAM; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 285 °C | 545 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | DAM; ISO 75-1/-2 | ||
|
Flammability, UL94
|
HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; IEC 60695-11-10 | ||
|
HB @Thickness 0.850 mm |
HB @Thickness 0.0335 in |
DAM; IEC 60695-11-10 | |||
| Flame Spread |
29.0 mm/min @Thickness 1.00 mm |
1.14 in/min @Thickness 0.0394 in |
Burning rate; ISO 3795 (FMVSS 302) | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | >= 320 °C | >= 608 °F | |||
| 325 °C | 617 °F | Optimum | |||
| <= 330 °C | <= 626 °F | ||||
| Mold Temperature | >= 140 °C | >= 284 °F | |||
| 150 °C | 302 °F | Optimum | |||
| <= 160 °C | <= 320 °F | ||||
| Drying Temperature |
100 °C @Time 21600 - 28800 sec |
212 °F @Time 6.00 - 8.00 hour |
|||
| Moisture Content | 0.100 % | 0.100 % | |||
|
De |
|||||
| Drying Recommended | yes | ||||
| Part Marking Code | >PA6T/XT-GF45< | ISO 11469 | |||
| >PPA-GF45< | SAE J1344 | ||||
| Processing | Injection Molding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PA6T/XT-GF45 | ISO 1043 | |||
| Special characteristics | Heat stabilized or stable to heat | ||||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb'sterms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.
Users viewing this material also viewed the following:
DuPont Performance Polymers Zytel? HTN51G45HSL NC010 PA6T/XT-GF45
DuPont Performance Polymers Zytel? HTN51G35HSLR BK420J PA6T/XT-GF35
DuPont Performance Polymers Zytel? HTN51G35HSLR BK420 PA6T/XT-GF35
DuPont Performance Polymers Zytel? HTN51G35HSL NC010 PA6T/XT-GF35
DuPont Performance Polymers Zytel? HTN51G35HSL BK083 PA6T/XT-GF35
免責聲明：（1）以上所展示的信息由企業自行提供，內容的真實性、準確性和合法性由發布企業負責，環球塑化網對此不承擔任何保證責任。我們原則上建議您優先選擇“塑企通”會員合作! （2）同時我們鄭重提醒各位買/賣家，交易前請詳細核實對方身份，切勿隨意打款或發貨，謹防上當受騙。如發現虛假信息，請向環球塑化網舉報。
簡繁切換