| SABIC Innovative Plastics LNP STAT-KON AE006 ABS | |||
|---|---|---|---|
| Categories: |
Polymer; Thermoplastic; ABS Polymer
|
||
| Material Notes: |
LNP* STAT-KON* AE006 is a compound based on ABS containing 30% Carbon Fiber. Added feature of this grade is: Electrically Conductive.
|
||
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. | ||
|
|||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Density | 1.21 g/cc | 0.0437 lb/in3 | ASTM D792 |
| Moisture Absorption | 0.180 % | 0.180 % | 50% RH, 24 hrs; ASTM D570 |
| 0.330 % | 0.330 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow |
0.00020 - 0.00040 cm/cm @Time 86400 sec |
0.00020 - 0.00040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse |
0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 128 MPa | 18600 psi | 5 mm/min; ISO 527 |
| 131 MPa | 19000 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.0 % | 1.0 % | 5 mm/min; ISO 527 |
| 1.1 % | 1.1 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.0 % | 1.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 18.64 GPa | 2704 ksi | 1 mm/min; ISO 527 |
| 20.0 GPa | 2900 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 182 MPa | 26400 psi | ISO 178 |
| 190 MPa | 27600 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 17.6 GPa | 2550 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 17.6 GPa | 2550 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.14 J/cm | 5.88 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 19.0 kJ/m2 | 9.04 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy |
8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1.0 - 4.0 ohm | 1.0 - 4.0 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow |
34.0 μm/m-°C @Temperature -30.0 - 30.0 °C |
18.9 μin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow |
38.0 μm/m-°C @Temperature -30.0 - 30.0 °C |
21.1 μin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
104 °C @Thickness 3.20 mm |
219 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
100 °C @Thickness 3.20 mm |
212 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb'sterms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.
Users viewing this material also viewed the following:
SABIC Innovative Plastics LNP STAT-KON ME006 PP
Teknor Apex Sinpolene MBB2666 Acrylonitrile Butadiene Styrene
Quadrant EPP Ketron? 1000 LSG PEEK, Biocompatibility tested (ISO Product Data Sheet)
SABIC Innovative Plastics LNP Stat-kon AD000Z ABS
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對此不承擔(dān)任何保證責(zé)任。我們原則上建議您優(yōu)先選擇“塑企通”會員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請?jiān)敿?xì)核實(shí)對方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請向環(huán)球塑化網(wǎng)舉報(bào)。
簡繁切換