| ABIC Innovative Plastics LNP STAT-KON AE002 ABS | |||
|---|---|---|---|
| Categories: |
Polymer; Thermoplastic; ABS Polymer
|
||
| Material Notes: |
LNP* STAT-KON* AE002 is a compound based on ABS resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive.
|
||
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. | ||
|
|||
Printer friendly version
Download as PDF
Download to Excel (requires Excel and Windows)
Export data to your CAD/FEA program| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in3 | ASTM D792 |
| 1.16 g/cc | 0.0419 lb/in3 | ISO 1183 | |
| Moisture Absorption | 0.230 % | 0.230 % | 50% RH, 24 hrs; ASTM D570 |
| 0.350 % | 0.350 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow |
0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse |
0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 82.0 MPa | 11900 psi | 5 mm/min; ISO 527 |
| 83.0 MPa | 12000 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 82.0 MPa | 11900 psi | 5 mm/min; ISO 527 |
| 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.4 % | 1.4 % | 5 mm/min; ISO 527 |
| 1.5 % | 1.5 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.4 % | 1.4 % | 5 mm/min; ISO 527 |
| 1.5 % | 1.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 7.38 GPa | 1070 ksi | 1 mm/min; ISO 527 |
| 7.65 GPa | 1110 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 108 MPa | 15700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 112 MPa | 16200 psi | ISO 178 | |
| Flexural Yield Strength | 114 MPa | 16500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 6.50 GPa | 943 ksi | 2 mm/min; ISO 178 |
| 6.66 GPa | 966 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.28 J/cm | 4.27 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m2 | 1.90 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m2 | 7.14 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy |
9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 2.0 - 4.0 ohm | 2.0 - 4.0 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow |
33.1 μm/m-°C @Temperature -30.0 - 30.0 °C |
18.4 μin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow |
82.5 μm/m-°C @Temperature -30.0 - 30.0 °C |
45.8 μin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
105 °C @Thickness 3.20 mm |
221 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
101 °C @Thickness 3.20 mm |
214 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb'sterms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.
Users viewing this material also viewed the following:
SABIC Innovative Plastics LNP STAT-KON AE006 ABS
SABIC Innovative Plastics LNP STAT-KON AE004 ABS
SABIC Innovative Plastics LNP STAT-KON AE003 ABS (Europe-Africa-Middle East)
SABIC Innovative Plastics LNP Stat-kon AD000Z ABS
SABIC Innovative Plastics LNP STAT-KON AD000 ABS