| | Category | Property | Metals | Trade Name | Manufacturer | |
|
|
| SABIC Innovative Plastics Lexan? 101R PC | |||
|---|---|---|---|
| Categories: |
Polymer; Thermoplastic; Polycarbonate (PC)
|
||
| Material Notes: |
UL rated HB as of 10/97. 200 series recommended when V-2 rating required. Nonhalogenated. 7.0 MFR, for thicker sections without sinks. Internal mold release.
|
||
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. | ||
|
|||
Printer friendly version
Download as PDF
Download to Excel (requires Excel and Windows)
Export data to your CAD/FEA program| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 | ||
| Density | 1.19 g/cc | 0.0430 lb/in3 | ASTM D792 | ||
| Water Absorption |
0.15 % @Time 86400 sec |
0.15 % @Time 24.0 hour |
ASTM D570 | ||
| Moisture Absorption at Equilibrium | 0.35 % | 0.35 % | ASTM D570 | ||
|
0.58 % @Temperature 100 °C |
0.58 % @Temperature 212 °F |
ASTM D570 | ||
| Linear Mold Shrinkage, Flow |
0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | ||
| Melt Flow |
7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 70 | 70 | ASTM D785 | ||
| Hardness, Rockwell R | 118 | 118 | ASTM D785 | ||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 | ||
| Elongation at Break | 135 % | 135 % | Type I, 50 mm/min; ASTM D638 | ||
| Elongation at Yield | 7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D638 | ||
| Flexural Yield Strength | 97.0 MPa | 14100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| Flexural Modulus | 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| Izod Impact, Notched | 9.07 J/cm | 17.0 ft-lb/in | ASTM D256 | ||
| Izod Impact, Unnotched | 32.04 J/cm | 60.02 ft-lb/in | ASTM D4812 | ||
| Tensile Impact Strength | 630 kJ/m2 | 300 ft-lb/in2 | Type S; ASTM D1822 | ||
| Dart Drop, Total Energy | 64.0 J | 47.2 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 | ||
| 169 J | 125 ft-lb | ASTM D3029 | |||
| Taber Abrasion, mg/1000 Cycles | 10 | 10 | CS-17, 1 kg; ASTM D1044 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | ASTM D257 | ||
|
Dielectric Constant
|
2.96 @Frequency 1.00e+6 Hz |
2.96 @Frequency 1.00e+6 Hz |
ASTM D150 | ||
|
3.17 @Frequency 50.0 - 60.0 Hz |
3.17 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |||
| Dielectric Strength |
14.9 kV/mm @Thickness 3.20 mm |
378 kV/in @Thickness 0.126 in |
in air; ASTM D149 | ||
|
Dissipation Factor
|
0.00090 @Frequency 50.0 - 60.0 Hz |
0.00090 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | ||
|
0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
ASTM D150 | |||
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | UL 746A | ||
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A | ||
| High Amp Arc Ignition, HAI | 60 - 120 arcs | 60 - 120 arcs | UL 746A | ||
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow |
68.4 μm/m-°C @Temperature -40.0 - 95.0 °C |
38.0 μin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 | ||
| Specific Heat Capacity | 1.25 J/g-°C | 0.299 BTU/lb-°F | ASTM C351 | ||
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft2-°F | ASTM C177 | ||
| Deflection Temperature at 0.46 MPa (66 psi) |
137 °C @Thickness 6.40 mm |
279 °F @Thickness 0.252 in |
unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) |
132 °C @Thickness 6.40 mm |
270 °F @Thickness 0.252 in |
unannealed; ASTM D648 | ||
| Vicat Softening Point | 154 °C | 309 °F | Rate B/50; ASTM D1525 | ||
| UL RTI, Electrical | 130 °C | 266 °F | UL 746B | ||
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | UL 746B | ||
| UL RTI, Mechanical without Impact | 130 °C | 266 °F | UL 746B | ||
| Flammability, UL94 |
HB @Thickness 0.710 mm |
HB @Thickness 0.0280 in |
UL 94 | ||
| Optical Properties | Metric | English | Comments | ||
| Refractive Index | 1.586 | 1.586 | ASTM D542 | ||
| Haze |
1.0 % @Thickness 2.54 mm |
1.0 % @Thickness 0.100 in |
ASTM D1003 | ||
| Transmission, Visible | 88 % | 88 % | 2.54 mm; ASTM D1003 | ||
|
De |
|||||
| Radiant Panel Listing | YES | UL Tested | |||
| Specific Volume | 0.83cm^3/g | ASTM D792 | |||
| UV-light, water exposure/immersion | F2 | UL 746C | |||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb'sterms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.
Users viewing this material also viewed the following:
SABIC Innovative Plastics Valox? 357U PBT+PC
PTS Tristar? PC-10R 10 MFI Polycarbonate With Release
SABIC Innovative Plastics Lexan? 101 PC
PTS Tristar? PC-06 6 MFI Extrusion Grade Polycarbonate
SABIC Innovative Plastics Lexan? FR60 Polycarbonate Film, Flame Retardant