| Lanxess Durethan? BKV 15 H.3 DUS008 000000 Nylon 6, 15% Glass Fiber | |||
|---|---|---|---|
| Categories: | Polymer; Thermoplastic; Nylon; Nylon 6; Nylon 6, 20% Glass Fiber Filled; Nylon 6, Heat Stabilized | ||
| Material Notes: |
PA 6, 15% glass fibers, injection molding, heat-ageing stabilized
Information provided by LANXESS. |
||
| Key Words: | ISO 1874-PA6, GHR,14-070,GF15 | ||
|
|
|
||
|
|||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.228 g/cc | 0.04436 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0035 cm/cm | 0.0035 in/in | 150x105x3, 280°C / MT 80°C; 500 bar; ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | 150x105x3, 280°C / MT 80°C; 500 bar; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 65.0 MPa | 9430 psi | conditioned, 5 mm/min; ISO 527-1,-2 |
| 130 MPa | 18900 psi | 5 mm/min; ISO 527-1,-2 | |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527-1,-2 |
| 12 % | 12 % | conditioned, 5 mm/min; ISO 527-1,-2 | |
| Tensile Modulus | 3.10 GPa | 450 ksi | conditioned, 1 mm/min; ISO 527-1,-2 |
| 6.50 GPa | 943 ksi | 1 mm/min; ISO 527-1,-2 | |
| Flexural Strength | 110 MPa | 16000 psi | conditioned, 2 mm/min; ISO 178-A |
| 205 MPa | 29700 psi | 2 mm/min; ISO 178-A | |
| Flexural Modulus | 3.10 GPa | 450 ksi | conditioned, 2 mm/min; ISO 178-A |
| 5.50 GPa | 798 ksi | 2 mm/min; ISO 178-A | |
Izod Impact, Notched (ISO) 
|
<= 10.0 kJ/m2 @Temperature 23.0 °C |
<= 4.76 ft-lb/in2 @Temperature 73.4 °F |
ISO 180-1A |
|
10.0 kJ/m2 @Temperature 23.0 °C |
4.76 ft-lb/in2 @Temperature 73.4 °F |
conditioned; ISO 180-1A | |
|
Izod Impact, Unnotched (ISO)
|
40.0 kJ/m2 @Temperature -30.0 °C |
19.0 ft-lb/in2 @Temperature -22.0 °F |
ISO 180-1U |
|
40.0 kJ/m2 @Temperature -30.0 °C |
19.0 ft-lb/in2 @Temperature -22.0 °F |
conditioned; ISO 180-1U | |
|
45.0 kJ/m2 @Temperature 23.0 °C |
21.4 ft-lb/in2 @Temperature 73.4 °F |
ISO 180-1U | |
|
85.0 kJ/m2 @Temperature 23.0 °C |
40.4 ft-lb/in2 @Temperature 73.4 °F |
conditioned; ISO 180-1U | |
|
Charpy Impact Unnotched
|
4.50 J/cm2 @Temperature -30.0 °C |
21.4 ft-lb/in2 @Temperature -22.0 °F |
ISO 179-1eU |
|
4.50 J/cm2 @Temperature -30.0 °C |
21.4 ft-lb/in2 @Temperature -22.0 °F |
conditioned; ISO 179-1eU | |
|
5.00 J/cm2 @Temperature 23.0 °C |
23.8 ft-lb/in2 @Temperature 73.4 °F |
ISO 179-1eU | |
|
10.0 J/cm2 @Temperature 23.0 °C |
47.6 ft-lb/in2 @Temperature 73.4 °F |
conditioned; ISO 179-1eU | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow |
30.0 μm/m-°C @Temperature 23.0 - 55.0 °C |
16.7 μin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow |
100 μm/m-°C @Temperature 23.0 - 55.0 °C |
55.6 μin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Melting Point | 220 °C | 428 °F | 10 °C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75-1,-2 |
| Shrinkage | 0.15 % | 0.15 % | post-shrinkage, 150x105x3, 120°C; 4 h; ISO 2577 |
| 0.15 % | 0.15 % | post-shrinkage, transverse, 150x105x3, 120°C; 4 h; ISO 2577 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 280 °C | 536 °F | Injection molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection molding; ISO 294 |
| Dry Time |
2.00 - 6.00 hour @Temperature 80.0 °C |
2.00 - 6.00 hour @Temperature 176 °F |
|
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer test |
中山市沙泊塑料有限公司:主要經營各種工程塑膠原料(新料和改性料),包括: ABS、LCP、PBT、PPS、TPE、TPU、PA6、PA66、PET、POM、PMMA、PC、PC/ABS、PC/PBT,等改性產品均符合SGS檢測報告。
業務部:李厚佳
Email:ppslcp@163.com
http://www.shabosl.com/
Tel:18219005688:李生
免責聲明：（1）以上所展示的信息由企業自行提供，內容的真實性、準確性和合法性由發布企業負責，環球塑化網對此不承擔任何保證責任。我們原則上建議您優先選擇“塑企通”會員合作! （2）同時我們鄭重提醒各位買/賣家，交易前請詳細核實對方身份，切勿隨意打款或發貨，謹防上當受騙。如發現虛假信息，請向環球塑化網舉報。
簡繁切換