性能項目 |
試驗條件[狀態] |
測試方法 |
測試數據 |
數據單位 |
||
|
基本性能 |
吸水率 |
24hr，in 23℃ |
ASTM D-570 |
0.20 |
% |
|
|
物理性能 |
透光率 |
厚度3mm |
ASTM D-1003 |
88 |
% |
|
|
阻燃性 |
厚度1.47mm (厚度3.05mm ) |
UL 94 |
94V-2 |
|
||
|
比重 |
|
ASTM D-792 |
1.20 |
|
||
|
折射率 |
|
ASTM D-542 |
1.585 |
|
||
|
機械性能 |
洛氏硬度 |
|
ASTM D-785 |
77 |
M標度 |
|
|
拉伸率 |
屈服點 |
- |
ASTM D-638 |
6 |
- |
|
|
斷裂點 |
- |
ASTM D-638 |
140 |
- |
||
|
彎曲模量 |
|
ASTM D-790 |
2230(22700) |
Mpa(kgf/cm2) |
||
|
拉伸強度 |
屈服點 |
- |
ASTM D-638 |
61(620) |
Mpa(kgf/cm2) |
|
|
斷裂點 |
- |
ASTM D-638 |
81(830) |
Mpa(kgf/cm2) |
||
|
拉伸模量 |
|
ASTM D-638 |
2120(21600) |
Mpa(kgf/cm2) |
||
|
彎曲強度 |
|
ASTM D-790 |
90(915) |
Mpa(kgf/cm2) |
||
|
壓縮強度 |
|
ASTM D-695 |
76(770) |
Mpa(kgf/cm2) |
||
|
耐沖擊強度值 |
艾氏、帶缺口厚度6.4mm |
ASTM D-256 |
140(14) |
j/m(kgf.cm/cm) |
||
|
耐沖擊強度值 |
艾氏、帶缺口厚度3.2mm |
ASTM D-256 |
880(90) |
j/m(kgf.cm/cm) |
||
|
電氣性能 |
體積電阻率 |
|
ASTM D-257 |
3 |
1016Ω.cm |
|
|
絕緣破壞強度 |
快速加壓值厚度1.6mm |
ASTM D-149 |
30 |
KV/mm |
||
|
介電率 |
60Hz(106Hz) |
ASTM D-150 |
2.95(2.9) |
|
||
|
耐導電徑跡性 |
CTI |
IEC 112 |
300 |
V |
||
|
耐電弧性 |
|
ASTM D-495 |
110 |
secc |
||
|
介電正切 |
60Hz(106Hz) |
ASTM D-150 |
0.0004(0.009) |
|
||
|
加工性能 |
成型收縮率 |
流動方向(垂直方向) |
ASTM D-955 |
0.5～0.7 |
% |
|
|
熱性能 |
線膨脹系數 |
流動方向(垂直方向) |
ASTM D-696 |
7 |
10-5cm/cm/℃ |
|
|
負荷撓曲溫度 |
負荷0.451MPa(4.6kgf/cm) |
ASTM D-648 |
143 |
℃ |
||
|
溫度指數 |
電學式 |
厚度1.47mm |
UL 746B |
125 |
°C |
|
|
沖擊式 |
厚度1.47mm |
UL 746B |
115 |
°C |
||
|
非沖擊式 |
厚度1.47mm |
UL 746B |
125 |
°C |
||
|
負荷撓曲溫度 |
負荷1.813MPa(18.6kgf/cm) |
ASTM D-648 |
143 |
℃ |
||