點擊圖片查看大圖③原料技術數據
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 物理性能
|
比重 | ASTM D792 | 1.25 |
g/cm³
|
|
| ISO 1183 | 1.26 |
g/cm³
|
|||
| 熔流率 |
240℃/2.16 kg
|
ASTM D1238 | 13 |
g/10 min
|
|
| 溶化體積流率 | 240℃/2.16 kg | ISO 1133 | 12.0 |
cm³/10min
|
|
| 收縮率 | 流動 | ASTM D955 | 1.6 |
%
|
|
|
橫向流量: 2.00 mm
|
ISO 294-4 | 1.7 | % | ||
|
流量: 2.00 mm
|
ISO 294-4 | 1.6 | % | ||
| 吸水率 |
23℃, 24 hr
|
ASTM D570, ISO 62 | 0.30 | % | |
| 飽和, 23℃ | ISO 62 | 0.60 | % | ||
|
平衡, 23℃, 50% RH
|
ISO 62 | 0.20 | % | ||
| 硬度 |
支撐 D
|
ASTM D2240, ISO 868 | 72 | ||
|
支撐 D，15秒
|
ISO 868 | 68 | |||
| 機械性能 |
拉伸模量 | 23℃ | ISO 527-2 | 525 |
MPa
|
| 拉伸應力 |
屈服, 23℃
|
ASTM D638 | 26.0 |
MPa
|
|
|
斷裂, 23℃
|
ISO 527-2 | 45.8 |
MPa
|
||
| 斷裂, 23℃ | ISO 527-2 | 53.0 |
MPa
|
||
|
5.0% 應變, 23℃
|
ASTM D638 | 14.0 |
MPa
|
||
|
10%應變, 23℃
|
ASTM D638 | 20.0 |
MPa
|
||
| 拉伸應變 | 屈服, 23℃ | ISO 527-2 | 25 |
%
|
|
| 斷裂, 23℃ | ASTM D638 | 360 |
%
|
||
| 斷裂, 23℃ | ISO 527-2 | 450 | % | ||
| 斷張率 | 23℃ | ISO 527-2 | 530 |
%
|
|
| 拉伸蠕變模量 |
1 hr
|
ISO 899-1 | 360 |
MPa
|
|
|
1000 hr
|
ISO 899-1 | 312 |
MPa
|
||
| 彎曲模量 | -40℃ | ASTM D790 | 2410 |
MPa
|
|
| 23℃ | ASTM D790 | 570 |
MPa
|
||
| 100℃ | ASTM D790 | 207 |
MPa
|
||
| -40℃ | ISO 178 | 2350 |
MPa
|
||
| 23℃ | ISO 178 | 550 |
MPa
|
||
| 100℃ | ISO 178 | 200 |
MPa
|
||
| Tensile Stress |
23℃, 5% Strain
|
ISO 527-2 | 23.0 | MPa | |
|
23℃, 10% Strain
|
ISO 527-2 | 14.0 | MPa | ||
| 簡支梁缺口沖擊強度 | -40℃ | ISO 179/1eA | 7.0 |
kJ/m²
|
|
| -30℃ | ISO 179/1eA | 10 |
kJ/m²
|
||
| 23℃ | ISO 179/1eA | 33 |
kJ/m²
|
||
| 懸壁梁缺口沖擊強度 | -40℃ | ASTM D256 | 40 |
J/m
|
|
| 23℃ | ASTM D256 | 210 |
J/m
|
||
| -40℃ | ISO 180/1A | 7.0 |
kJ/m²
|
||
| 23℃ | ISO 180/1A | 38 |
kJ/m²
|
||
| 拉伸沖擊強度 | 23℃ | ISO 8256 | 300 |
kJ/m²
|
|
| 熱性能
|
熱變形溫度 | 0.45 MPa, 未退火 | ASTM D648 | 130 | ℃ |
| 0.45 MPa, 未退火 | ISO 75-2/B | 95.0 | ℃ | ||
|
1.8 MPa, 未退火
|
ASTM D648 | 52.0 | ℃ | ||
|
1.8 MPa, 未退火
|
ISO 75-2/B | 45.0 | ℃ | ||
| 脆化溫度 | ISO 974 | -97.0 | ℃ | ||
| 玻璃轉化溫度 | ISO 11357-2 | 25.0 | ℃ | ||
| 熔融溫度 2 | ISO 11357-3, ASTM D3418 | 218 | ℃ | ||
| 線形膨脹系數 | 流動: -40 到 23℃ | ASTM E831, ISO 11359-2 | 0.00013 |
cm/cm/℃
|
|
| 流動: 23 到 55℃ | ASTM E831, ISO 11359-2 | 0.00017 | cm/cm/℃ | ||
| 流動: 55 到 120℃ | ASTM E831, ISO 11359-2 | 0.00017 | cm/cm/℃ | ||
|
流動: 23 到 55℃
|
ISO 11359-2 | 0.00018 | cm/cm/℃ | ||
| 橫向: -40 到 23℃ | ASTM E831, ISO 11359-2 | 0.00013 | cm/cm/℃ | ||
| 橫向: 23 到 55℃ | ASTM E831, ISO 11359-2 | 0.00018 | cm/cm/℃ | ||
| 橫向: 55 到 120℃ | ASTM E831, ISO 11359-2 | 0.00018 | cm/cm/℃ | ||
|
橫向: 23 到 55℃
|
ISO 11359-2 | 0.00017 | cm/cm/℃ | ||
| 電氣性能 |
表面電阻率 | IEC 60093 |
1.0E+15
|
ohms
|
|
| 體積電阻率 | IEC 60093 |
2.0E+12
|
ohm·cm
|
||
| 介電強度 |
23℃, 1.91 mm 3
|
ASTM D149 | 18 | kV/mm | |
| 23℃ | IEC 60243-1 | 20 |
kV/mm
|
||
| 介電常數 |
23℃, 1.91 mm, 100 Hz
|
ASTM D150 | 4.00 | ||
|
23℃, 1.91 mm, 1 kHz
|
ASTM D150 | 3.90 | |||
|
23℃, 1.91 mm, 1 MHz
|
ASTM D150 | 3.50 | |||
|
23℃, 100 Hz
|
IEC 60250 | 4.00 | |||
|
23℃, 1 Hz
|
IEC 60250 | 3.50 | |||
| 耗散因數 |
23℃, 1.91 mm, 100 Hz
|
ASTM D150 | 1.016 | ||
|
23℃, 1.91 mm, 1Hz
|
ASTM D150 | 0.019 | |||
|
23℃, 1.91 mm, 1Hz
|
ASTM D150 | 0.030 | |||
|
23℃, 100 Hz
|
IEC 60250 | 0.016 | |||
|
23℃, 1 Hz
|
IEC 60250 | 0.030 | |||
| 漏電起痕指數 | IEC 60112 |
> 600
|
V
|
||
| UL 阻燃等級 | 1.50 mm | UL 94 | HB | ||
|
3.00 mm
|
UL 94 | HB | |||
| 可燃性等級 | 1.50 mm | IEC 60695-11-10, -20 |
HB
|
||
| 極限氧指數 | ISO 4589-2 | 23 |
%
|
||
| RTI Str | 1.50 mm | UL 746 | 50.0 | ℃ | |
| RTI Imp | 1.50 mm | UL 746 | 50.0 | ℃ | |
| RTI Elec | 1.50 mm | UL 746 | 50.0 | ℃ | |
| 其它 | 干燥溫度 | 110 | ℃ | ||
| 干燥時間 |
2.0 到 3.0
|
hr | |||
| 建議的大水分含量 |
< 0.080
|
% | |||
| Extrusion Melt Temperature | Optimum |
235
|
℃ | ||