Lubrizol Pellethane? 2363-80AE Thermoplastic Polyurethane Elastomer 物性表
?
物理性能額定值 (公制)額定值 (英制)測試方法
| 密度 | 1.12 g/cc | 0.0405 lb/in3 | ASTM D792 |
| 線性成型收縮率 |
0.0050 - 0.0080 cm/cm
@Thickness 1.59 mm
|
0.0050 - 0.0080 in/in
@Thickness 0.0625 in
|
plaque |
| 線性成型收縮率，橫向 |
-0.00100 - 0.0040 cm/cm
@Thickness 1.59 mm
|
-0.00100 - 0.0040 in/in
@Thickness 0.0625 in
|
plaque |
| 熔體流動速率 |
10 g/10 min
@Load 2.16 kg, Temperature 224 °C
|
10 g/10 min
@Load 4.76 lb, Temperature 435 °F
|
ASTM D1238 |
?
機械性能額定值 (公制)額定值 (英制)測試方法
| 肖氏硬度 (邵氏 A) | 81 - 89 | 81 - 89 | ASTM D2240 |
| 極限抗拉強度 | 28.9 MPa | 4190 psi | ASTM D412 |
| 伸長率 (斷裂) | 550 % | 550 % | ASTM D412 |
| 50% Modulus | 0.00480 GPa | 0.696 ksi | ASTM D412 |
| 模量 | 0.00610 GPa | 0.885 ksi | ASTM D412 |
| 300％模量 | 0.0103 GPa | 1.49 ksi | ASTM D412 |
| 撕裂強度 | 73.6 kN/m | 420 pli | Die C; ASTM D624 |
| 泰伯磨損，毫克/1000次 | 30 | 30 | H22 Wheel, 1000g; ASTM D1044 |
| 壓縮變形 |
30 %
@Temperature 25.0 °C, Time 79200 sec
|
30 %
@Temperature 77.0 °F, Time 22.0 hour
|
ASTM D395 Method B |
|
80 %
@Temperature 70.0 °C, Time 79200 sec
|
80 %
@Temperature 158 °F, Time 22.0 hour
|
ASTM D395 Method B | |
| Tensile Set | 70 % | 70 % | Elongation set after break; ASTM D412 |
熱性能額定值 (公制)額定值 (英制)測試方法
| 線性熱膨脹系數 |
165 μm/m-°C
@Temperature 20.0 °C
|
91.7 μin/in-°F
@Temperature 68.0 °F
|
ASTM D696 |
| 維卡軟化溫度 | 81.7 °C | 179 °F | ASTM D1525 |
| 玻璃化轉變溫度，Tg | -47.0 °C | -52.6 °F |
加工性能額定值 (公制)額定值 (英制)測試方法
| 加工（熔體）溫度 | 190 - 205 °C | 374 - 401 °F | Molding |
| 190 - 205 °C | 374 - 401 °F | Extrusion | |
| 模具溫度 | 15.0 - 60.0 °C | 59.0 - 140 °F | |
| 干燥溫度 | 80.0 - 95.0 °C |
176 - 203 °F |