CELCON? M90-45 XAP? CC34193 DK GRAY 136B
CELCON? M90-45 XAP? CC34466 GRAY #2 138B
CELCON? M90-45 XAP? CC34643 GRAY 105B
CELCON? M90-45 XAP? CD34611 BLACK 201B
CELCON? M90-45 XAP? CF2001 NATURAL
CELCON? M90-45 XAP? CV34644 SAND 457B
CELCON? M90-45 XAP? CY34815 BROWN 453B
CELCON M90-45XAP? | POM | Specialty
Descript ion
Celcon? acetal copolymer grade M90-45XAP? is a UV resistant, low emission
version, medium viscosity polymer providing optimum performance in general
purpose injection molding primarily for the interior automotive market. This
grade provides overall excellent performance in many applications.
Celcon? M90-45XAP? is formulated in custom colors for Toyota interior UV
stabilized applications
| ISO Data | Mechanical properties | Value | Unit | Test Standard |
| Phys | Density | 1410 | kg/m3 | ISO 1183 |
| Melt volume rate (MVR) | 8 | cm3/10min | ISO 1133 | |
| MVR test temperature | 190 | ℃ | ISO 1133 | |
| MVR test load | 2.16 | kg | ISO 1133 | |
| Mold shrinkage - parallel | 2.5 | % | ISO 294-4 | |
| Mold shrinkage - normal | 2.4 | % | ISO 294-4 | |
| Mech | Mechanical properties | Value | Unit | Test Standard |
| Tensile modulus (1mm/min) | 2650 | MPa | ISO 527-2/1A | |
| Tensile stress at yield (50mm/min) | 64 | MPa | ISO 527-2/1A | |
| Tensile strain at yield (50mm/min) | 9 | % | ISO 527-2/1A | |
| Flexural modulus (23℃) | 2450 | MPa | ISO 178 | |
| Flexural strength (23℃) | 77 | MPa | ISO 178 | |
| Charpy notched impact strength @ 23℃ | 6 | kJ/m2 | ISO 179/1eA | |
| Charpy notched impact strength @ -30℃ | 4 | kJ/m2 | ISO 179/1eA | |
| Notched impact strength (Izod) @ 23℃ | 6 | kJ/m2 | ISO 180/1A | |
| Therm | Thermal properties | Value | Unit | Test Standard |
| Melting temperature (10℃/min) | 167 | ℃ | ISO 11357-1,-2,-3 | |
| DTUL @ 1.8 MPa | 91 | ℃ | ISO 75-1/-2 | |
| DTUL @ 0.45 MPa | 151 | ℃ | ISO 75-1/-2 | |
| Coeff.of linear therm. expansion (parallel) | 1.1 | E-4/℃ | ISO 11359-2 | |
| Coeff.of linear therm. expansion (normal) | 1.2 | E-4/℃ | ISO 11359-2 |
Processing
Pre Drying
Drying is recommended to achieve lowest emission performance. If material
contacts moisture through improper storage or handling, drying may be necessary
to prevent splay and odor issues.
Drying time (h):3