This datasheet of Ultramid® N-265 NF3001 from BASF is provided by the international plastics database CAMPUS.

　　PA66+GF+MF.專業(yè)從事PA(尼龍)改性。主要有：尼龍PA66+GF玻纖，PA66+CF碳纖,PA66+MoS2二硫化鉬、PA66+PTFE聚四氟乙烯，PA66+鐵氟龍耐磨、PA66+GP石墨、PA66+GB玻璃微珠等;

　　一、增強PA66:PA66-10GF,PA66-15GF,PA66-20GF,PA66-25GF,PA66-30GF,PA66-35GF,PA66-40GF,PA66-50GF,等各種規(guī)格;

　　二、增韌尼龍66，超韌PA66，耐寒PA66，耐低溫尼龍，耐候PA66，增韌尼龍耐低溫零下40度，性能等同于ST801與ST8018,

　　三、尼龍增強、增韌、阻燃、耐磨、耐候、耐油、耐水解、耐高(低)溫、耐熱等改性產(chǎn)品，

　　機械性能 - 熱性能 - 其它性能

　　Ultramid® N-265 NF3001 | PA66-MF40 | BASF

　　材料文字說明

　　Ultramid® N-265 NF3001 is a general purpose, 40% mineral reinforced PA6/6 that provides excellent flatness and dimensional stability in injection molding.

　　top

　　機械性能干 / 已調(diào)節(jié)單位Test Standard

　　拉伸模量9900 / -MPaISO 527-1/-2

　　斷裂應力100 / -MPaISO 527-1/-2

　　斷裂伸長率3 / -%ISO 527-1/-2

　　無缺口簡支梁沖擊強度 (+23°C)30 / -kJ/m²ISO 179/1eU

　　無缺口簡支梁沖擊強度 (-30°C)25 / -kJ/m²ISO 179/1eU

　　簡支梁缺口沖擊強度 (+23°C)3 / -kJ/m²ISO 179/1eA

　　top

　　熱性能干 / 已調(diào)節(jié)單位Test Standard

　　熔融溫度 (10°C/min)257 / *°CISO 11357-1/-3

　　熱變形溫度 (1.80 MPa)215 / *°CISO 75-1/-2

　　熱變形溫度 (0.45 MPa)240 / *°CISO 75-1/-2

　　top

　　其它性能干 / 已調(diào)節(jié)單位Test Standard

　　吸水性5.1 / *%類似ISO 62

　　吸濕性1.5 / *%類似ISO 62

　　密度1500 / -kg/m³ISO 1183

　　top

　　典型數(shù)據(jù)

　　地區(qū)供應

　　北美

　　top

　　其他信息

　　注塑成型

　　PA66 materials must be properly dried in order to provide parts with optimum strength and toughness. PA66 materials are hygroscopic and will become degraded by excessive moisture during the injection molding process. For unopened bag/box, dry at 140F (60°C) for 1-2 hours. For material exposed to the atmosphere, if additional drying is needed, dry at 150F (66°C) or until the moisture level is between 0.04 - 0.20%.

　　Melt Temperature: 288 - 305°C (550 - 580F)

　　Mold Temperature: 6 0 - 100°C (140 - 212F)

　　Injection Pressure: 35 - 125 MPa (5000 - 18000 psi)

　　Back Pressure: 0 - 0.35 MPa (0 - 50 psi)

　　Screw RPM 40 - 80

　　Screw Compression Ratio:3:1 - 4:1

　　This product can be processed over a wide range of mold temperatures; however, for applications where aesthetics are critical, a mold surface temperature of 60-100°C (140-212F) is recommended.

　　Injection pressure controls the filling of the part and should be applied for 90% of ram travel. Pac king pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off.

　　Fast fill rates are recommended to insure uniform melt delivery to the cavity and prevent premature freezing.